熔融石英

熔融石英是以優質的東海石英為原料，經挑選、粗破碎、磁選除鐵、酸洗、烘干粗細磨、整形分篩等一系列工藝加工而成。由于經1700C-2500C高溫燒制后轉化而成的熔融型或無定形石英，石英晶體結構產生改變，使熔融石英比天然結晶型石英純度更高、比重和熱膨脹系數較低，外觀為無色透明，有少部分乳白霧狀氣泡，可按用戶要求粒度加工。

Fused quartz and fused silica are types of glass containing primarily silica in amorphous (non-crystalline) form. They are manufactured using several different processes. Note that glasses formed by the traditional 'melt-quench' methods (heating the material to melting temperatures, then rapidly cooling to the solid glass phase), are often referred to as 'vitreous', as in 'vitreous silica'. The term 'vitreous' is synonymous with 'glass', when used in the melt-quench context.

Fused quartz is manufactured by melting naturally occurring quartz crystals of high purity at approximately 2000°C, using either an electrically heated furnace (electrically fused) or a gas/oxygen-fuelled furnace (flame fused). Fused quartz is normally transparent.

Fused quartz can also form naturally. The naturally occurring form is usually referred to as Metaquartzite and is formed under metamorphic conditions. An increase in heat causes the crystals within the quartz to become fused together.

Fused silica is produced using high purity silica sand as the feedstock, and is normally melted using an electric furnace, resulting in a material that is translucent or opaque. (This opacity is caused by very small air bubbles trapped within the material.)

Synthetic fused silica is made from a silicon-rich chemical precursor usually using a continuous flame hydrolysis process which involves chemical gasification of silicon, oxidation of this gas to silicon dioxide, and thermal fusion of the resulting dust (although there are alternative processes). This results in a transparent glass with an ultra-high purity and improved optical transmission in the deep ultraviolet. One common method involves adding silicon tetrachloride to a hydrogen-oxygen flame, however use of this precursor results in environmentally unfriendly by-products including chlorine and hydrochloric acid. To eliminate these by-products, new processes have been developed using an alternative feedstock, which has also resulted in a higher purity fused silica with further improved deep ultraviolet transmission.

Fumed silica is manufactured by a similar flame hydrolysis process to synthetic fused silica, however it is in the form of a fine powder/dust and is typically used in applications such as fillers for rubbers and plastics, coatings, adhesives, cements, sealants, cosmetics, pharmaceuticals, inks and abrasives.

The optical and thermal properties are superior to those of other types of glass due to its purity (or rather, its lack of impurities). For these reasons, it finds use in situations such as semiconductor fabrication and laboratory equipment. It has better ultraviolet transmission than most other glasses, and so is used to make lenses and other optics for the ultraviolet spectrum. Its low coefficient of thermal expansion also makes it a useful material for precision mirror substrates.

特性：幾近零的熱膨脹率、的熱穩定性、純度高（SiO2含量高，鐵、鉀、鈉、鈦等含量低）、化學性質穩定、專用機械控制生產、粒度分布穩定。

Properties： hardly coefficient of thermal expansion,excellent thermal stability、high purity、steady chemical property and distribution of(particle)size.

主要用途：環氧樹脂澆注、電子密封料、鑄造材料、耐火、陶瓷和玻璃行業原料、涂料、油漆行業原料等。

Main uses：epoxy resin pouring、electronic seal、foundry、ceramic，glasswork、paint etc.

熔融石英根據產品規格分為熔融石英塊、熔融石英砂、熔融石英粉。

1、熔融石英塊

Fused Quartz Lump

規格： 1-100mm

成份：SiO2:99.95%-99.99%;

Fe2O3:45 ppM max; Al2O3:50 ppM-100 ppM;

K2O:45 ppM max; Na2O:45 ppM max;

Li2O:2.0 ppM max; EC:1.8-2.2; PH:5.8

Spec： 1-100mm

Constituents：SiO2:99.95%-99.99%;

Fe2O3:45 ppM max; Al2O3:50 ppM-100 ppM;

K2O:45 ppM max; Na2O:45 ppM max;

Li2O:2.0 ppM max; EC:1.8-2.2; PH:5.8

2、熔融石英砂 Fused Silica Sand

規格：0.1-15mm

成份：SiO2:99.95%-99.99%min;

Fe2O3:50 ppM max; Al2O3:50 ppM-100 ppM;

K2O:50 ppM max; Na2O:50 ppM max;

Li2O:2.0 ppM max; EC:1.8-2.2 ; PH: 5.8

Spec：0.1-15mm

Constituents：SiO2:99.95%-99.99%min;

Fe2O3:50 ppM max; Al2O3:50 ppM-100 ppM;

K2O:50 ppM max; Na2O:50 ppM max;

Li2O:2.0 ppM max; EC:1.8-2.2 ; PH: 5.8

3、熔融石英粉Fused Quartz Powder

規格：100-325目，325目-500目，500目，800目，1250目，1500目

成份：SiO2:99.93%-99.95%min;

Fe2O3:60 ppM max; Al2O3:60 ppM-500 ppM;

K2O:60 ppM max; Na2O:60 ppM max;

Li2O:2.0 ppM max; EC:1.8-2.2 ; PH: 6

Spec(mesh)：100-325，325 -500，500，800，1250，1500

Constituents：SiO2:99.93%-99.95%min;

Fe2O3:60 ppM max; Al2O3:60 ppM-500 ppM;

K2O:60 ppM max; Na2O:60 ppM max;

Li2O:2.0 ppM max; EC:1.8-2.2 ; PH: 6

主營行業： 公司注冊地址： 法人代表：張偉儒
員工人數： 廠房面積： 年營業額：
年進口額： 年出口額： 主要市場：,,
客戶群：
公司名稱:中材高新江蘇硅材料有限公司
注冊資本: 公司網址：http://jssinoma.glass.com.cn

聯系人：王總
電話：86-0518-87263988-
移動電話：15151291827
傳真：86---
地址：江蘇東海
網址：http://jssinoma.glass.com.cn

地區：江蘇 連云港 東海縣
網址: http://jssinoma.glass.com.cn

石英砂是石英石經破碎加工而成的石英顆粒。石英石（quartzrock）亦稱硅石，是一種質地堅硬、耐磨、化學性質穩定的硅酸鹽類礦物。在自然界中以石英砂巖、石英巖和脈石英存在。石英砂巖是固結的碎屑巖石，石英碎屑含量達95%以上，精制石英砂來源于各種巖漿巖，沉積巖和變質巖，重質礦物較少，伴生礦物為長石、云母和黏土礦物。石英巖分沉積成因和變質成因兩種，前者碎屑顆粒與膠結物的界限不明顯，后者指變質程度深、質純的石英巖礦石。脈石英是由熱液作用形成，幾乎全部由石英組成，致密塊狀構造。石英砂中礦物含量變化較大，以石英為主，其次為長石、云母、巖屑、重礦物、黏土礦物等。石英砂是一種堅硬、耐磨、化學性能穩定的硅酸鹽礦物，其主要礦物成分是SiO2，石英砂的顏色為乳白色、或無色半透明狀，硬度7，性脆無解理，貝殼狀斷口，油脂光澤，密度為2.65，堆積密度（1-20目為1.6），20-200目為1.5，其化學、熱學和機械性能具有明顯的異向性，不溶于酸，微溶于KOH溶液，熔點1750℃。石英砂常用規格有：0.5-1mm、1-2mm、2-4mm、4-8mm、8-16mm、16-32mm、10-20目、20-40目、40-80目、100-120目